Filament Polymaker PolyLite ASA 1,75mm 1kg - White
Bestseller
- Product Code:
- 66226530
157 GEL
Properties
- Filament diameter
- 1.75 mm
Features
- Color
- White
Material
- Filament material
- ASA
Other features
- Brand
- Polymaker
Weight & dimensions
- Weight
- 1 kg
Description
Product description: Filament Polymaker PolyLite ASA 1.75 mm 1 kg - White
PolyLite ASA from Polymaker is an alternative to ABS filaments with similar mechanical properties, but with increased resistance to harsh weather conditions and a less perceptible smell produced during printing. The material is distinguished by exceptionally high resistance to UV radiation, heat and moisture. Prints made of PolyLite ASA filament can be exposed to external factors without the risk of damage. On a cardboard , 100% recycled spool there is 1 kg of white filament with a diameter of 1.75 mm .
For large size prints, PolyLite ASA will require a printer with an enclosed build chamber .
Polymaker PolyLite ASA filament 1.75 mm 1 kg - White.
PolyLite ASA series filaments have a very wide range of applications.
PolyLite ASA filament properties
- High resistance to UV radiation, heat and moisture
- Possibility of exposing printouts to external factors
- The Vicat softening point is 105.3°C
- High impact resistance
- Slightly perceptible fragrance
- Easy processing
- Matte finish
Suggested filament printing parameters printing temperature From 240°C to 260°C table temperature From 75°C to 95°C Cooling Not recommended Due to the differences in the construction of printers, the above data should be treated as guidelines, and the appropriate values should be determined experimentally.
Technical specification and physical properties of the filament Parameter Range Filament diameter 1.75mm Color white Print speed From 30mm/s to 50mm/s printing temperature From 240°C to 260°C table temperature From 75°C to 95°C Material density 1.13g/cm³ Spool - material Polylite ASA Desiccant Yes Vacuum packing Yes net weight 1 kg
Useful links
- Manufacturer's website
- Technical Documentation